In the present study, warm hydroforming of cell phone cases with magnesium alloy AZ31 sheets was investigated. Fine-grained magnesium alloy sheets were prepared by cross rolling. And the tensile tests were first conducted in order to determine the proper forming temperature. The results showed that the most suitable temperature range appears to be 150-200 degrees C. At last, the magnesium alloy cell phone cases characterized with the small round radius of all edges were formed successfully at 170 degrees C with the low punch velocity and the maximum pressure not less than 5MPa.

Warm Hydroforming of Magnesium Alloy AZ31 Sheets / Zhang, S. H.; Ren, L. M.; Zhou, L. X.; Xu, Y. C.; Palumbo, Gianfranco; Tricarico, Luigi. - 546-549:(2007), pp. 333-336.

Warm Hydroforming of Magnesium Alloy AZ31 Sheets

PALUMBO, Gianfranco;TRICARICO, Luigi
2007-01-01

Abstract

In the present study, warm hydroforming of cell phone cases with magnesium alloy AZ31 sheets was investigated. Fine-grained magnesium alloy sheets were prepared by cross rolling. And the tensile tests were first conducted in order to determine the proper forming temperature. The results showed that the most suitable temperature range appears to be 150-200 degrees C. At last, the magnesium alloy cell phone cases characterized with the small round radius of all edges were formed successfully at 170 degrees C with the low punch velocity and the maximum pressure not less than 5MPa.
2007
Progress in Light Metals, Aerospace Materials and Superconductors : Proceedings: 2006 Beijing International Materials Week, June 25-30, 2006, Beijing, China
978-0-87849-432-3
Trans Tech Publications
Warm Hydroforming of Magnesium Alloy AZ31 Sheets / Zhang, S. H.; Ren, L. M.; Zhou, L. X.; Xu, Y. C.; Palumbo, Gianfranco; Tricarico, Luigi. - 546-549:(2007), pp. 333-336.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11589/10970
Citazioni
  • Scopus 6
  • ???jsp.display-item.citation.isi??? 5
social impact