Caratterizzazione Meccanica Di Compositi Rinforzati In Fibra Di Carbonio Con Emissioni Acustiche

Carbon Fiber Reinforced Plastic materials (CFRP) offer high specific mechanical properties that make them extremely attractive for aeronautical and aerospace applications. Anyway, their damaging mechanical response is very negative and, if these damages are not visible on the surface their use could become deeply dangerous if not properly monitored. It is therefore essential to detect, evaluate and analyze the several types of propagation of damage caused by static, cyclic and environmental effects. Acoustic Emission technique (AE) is an innovative methodology that is finding good evidence in detecting and identifying CFRP damage mechanisms. In this paper, the AE technique was applied to CFRP specimens subjected to open hole testing and mode I delamination.

Le materie plastiche rinforzate con fibre di carbonio (CFRP) offrono elevate proprietà meccaniche specifiche che le rendono estremamente interessanti per utilizzi in campo aeronautico e aerospaziale. Tuttavia, la loro risposta meccanica in condizioni di danneggiamento è molto compromessa e, se si considera la possibilità che tali danneggiamenti non siano visibili in superficie è facile immaginare quanto il loro utilizzo sia pericoloso se non opportunamente monitorato. Diventa quindi indispensabile rilevare, valutare ed analizzare i diversi tipi di propagazione dei danni causati da carichi statici, ciclici e da effetti ambientali. La tecnica delle emissioni acustiche (AE) rappresenta una metodologia innovativa che sta trovando buoni riscontri nella rilevazione e nell’identificazione dei meccanismi di danneggiamento dei CFRP. In questo lavoro la tecnica AE è stata applicata su provini CFRP sottoposti a test open-hole e delaminazione modo I.