Saldatura ibrida laser-arco della lega di titanio Ti6Al4V: caratterizzazione meccanica dei giunti e tolleranza al gap

The present research deals with the studies on mechanical characteristics of butt joint in Ti6A14V titanium alloy sheets of 3.0 mm thickness, comparing the welded joints obtained by laser beam welding without filler material and by laser-arc hybrid welding. These studies were performed by measuring Vickers hardness in the cross-sections obtained by welding. In particular the influence of the gap between the test sheets welded by laser CO2-MIG hybrid process has been analyzed. The morphological analysis of cross-section of welded joints obtained by different gaps has also been studied. Welded joints were characterized by tensile test and the deformation behaviour of welded joints by an optical measurement system of deformation based on the acquisition of stereoscopic images (ARAMIS 3D system). *** Nell’articolo sono riportati i risultati di un confronto tra le caratteristiche meccaniche di giunti testa a testa di lamiere in lega di titanio Ti6Al4V di spessore 3.0 mm, realizzati mediante saldatura con fascio laser senza materiale d’apporto e mediante saldatura ibrida laser-arco. Sono stati eseguiti rilievi di durezza Vickers nelle sezioni trasversali dei cordoni di saldatura ottenuti. In particolare è stata analizzata l’influenza del gap tra le amiere in prove di saldatura con tecnologia ibrida laser CO2-MIG. È stata eseguita l’analisi morfologica delle sezioni trasversali dei cordoni di saldatura ottenuti con diversi gap. I giunti saldati sono stati sottoposti a prove di trazione e il comportamento deformativo del giunto è stato analizzato tramite un sistema ottico di misura delle deformazioni basato sull’acquisizione stereoscopica delle immagini (sistema di analisi ARAMIS 3D).