This paper aims to analyze the effects of a corrosive atmosphere on sintered stainless steel (316L) samples. In particular, the relationship between resistance to corrosion and weight, density and tensile mechanical properties were investigated. Three groups of sintered stainless steel (316L) were studied, each of them characterized by laser power and scanning speed. For each group 9 specimens were prepared. For all of them, measurements of both weight and density were performed. One specimen for each group was tested, as received, for tensile mechanical test; the remaining 8 specimens of each group were subjected to a neutral salt spray (NSS) to evaluate the corrosion resistance of the studied material. Four different exposure periods were selected from the standard. At the end of each exposure period, two specimens per group were removed from the corrosion chamber and analyzed in order to study and record all the changes that were made.
Questo lavoro si propone di analizzare gli effetti di un ambiente corrosivo su campioni in acciaio inossidabile 316L sinterizzato. In particolare, si è analizzata la relazione esistente tra resistenza alla corrosione e peso, densità e proprietà meccaniche a trazione. Sono stati studiati tre gruppi di acciaio inossidabile 316L sinterizzato, diversi tra loro per potenza laser e per velocità di scansione. Per ogni gruppo sono stati preparati 9 provini e su tutti sono state eseguite misure sia di peso che di densità. Un provino per ogni gruppo è stato testato a trazione senza aver subito alcun trattamento corrosivo, i restanti 8 esemplari di ogni gruppo sono stati sottoposti ad atmosfera con soluzione salina neutra (NSS) per valutare la resistenza alla corrosione del materiale oggetto di studio. Sono stati definiti quattro diversi periodi di esposizione selezionati tra quelli previsti nella normativa di riferimento. Alla fine di ogni periodo di esposizione, due provini per gruppo sono stati rimossi dalla camera di corrosione e analizzati al fine di studiare e registrare tutte le modifiche subite
Effetti Della Corrosione Sulle Proprietà Meccaniche Di Sinterizzati In Acciaio Inossidabile / Barile, C.; Casavola, C.. - STAMPA. - (2017). (Intervento presentato al convegno 45° Convegno Nazionale AIAS – Associazione Italiana Per L’analisi Delle Sollecitazioni tenutosi a Pisa nel 6-9 Settembre 2017).
Effetti Della Corrosione Sulle Proprietà Meccaniche Di Sinterizzati In Acciaio Inossidabile
Barile C.
;Casavola C.
2017-01-01
Abstract
This paper aims to analyze the effects of a corrosive atmosphere on sintered stainless steel (316L) samples. In particular, the relationship between resistance to corrosion and weight, density and tensile mechanical properties were investigated. Three groups of sintered stainless steel (316L) were studied, each of them characterized by laser power and scanning speed. For each group 9 specimens were prepared. For all of them, measurements of both weight and density were performed. One specimen for each group was tested, as received, for tensile mechanical test; the remaining 8 specimens of each group were subjected to a neutral salt spray (NSS) to evaluate the corrosion resistance of the studied material. Four different exposure periods were selected from the standard. At the end of each exposure period, two specimens per group were removed from the corrosion chamber and analyzed in order to study and record all the changes that were made.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.