The aim of the work is to analyze the laser welding quality of USIBOR®1500-AS, without the coating removing. Through metallographic analysis, the martensitic phase was found both in the Fused Zone and in the Heat Affected Zone. Within the Fused Zone was, also, found a certain amount of Al-Si coating, which essentially depended on the welding speed. That coating modified the molten pool solidification mechanism, but did not affect the welds characteristics, in terms of defects and hardness. The welding speed did not affect the hardness values, while strongly influenced the Fused Zone and Heat Affected Zone widths.

Study on properties and microstructure of laser beam butt welded joints of Al-Si coated USIBOR® 1500 steel

Contuzzi N.;Palmieri M. E.;Angelastro A.
2022

Abstract

The aim of the work is to analyze the laser welding quality of USIBOR®1500-AS, without the coating removing. Through metallographic analysis, the martensitic phase was found both in the Fused Zone and in the Heat Affected Zone. Within the Fused Zone was, also, found a certain amount of Al-Si coating, which essentially depended on the welding speed. That coating modified the molten pool solidification mechanism, but did not affect the welds characteristics, in terms of defects and hardness. The welding speed did not affect the hardness values, while strongly influenced the Fused Zone and Heat Affected Zone widths.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11589/243062
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • Scopus 0
  • ???jsp.display-item.citation.isi??? ND
social impact