Shape-control by microwave-assisted hydrothermal method for the synthesis of magnetite nanoparticles using organic additives

A simple and fast microwave-assisted hydrothermal method is proposed for the synthesis of magnetite nanoparticles. The addition of different surfactants (polyvinylpyrrolidone, oleic acid, or trisodium citrate) was studied to investigate the effect on size distribution, morphology, and functionalization of the magnetite nanoparticles. Microwave irradiation at 150 degrees C for 2 h of aqueous ferrous chloride and hydrazine without additives resulted in hexagonal magnetite nanoplatelets with a facet-to-facet distance of 116 nm and a thickness of 40 nm having a saturation magnetization of similar to 65 Am-2 kg(-1). The use of polyvinylpyrrolidone led to hexagonal nanoparticles with a facet-to-facet distance of 120 nm and a thickness of 53 nm with a saturation magnetization of similar to 54 Am-2 kg(-1). Additives such as oleic acid and trisodium citrate yielded quasi-spherical nanoparticles of 25 nm in size with a saturation magnetization of similar to 70 Am-2 kg(-1) and spheroidal nanoparticles of 60 nm in size with a saturation magnetization up to similar to 82 Am-2 kg(-1), respectively. A kinetic control of the crystal growth is believed to be responsible for the hexagonal habit of the nanoparticles obtained without additive. Conversely, a thermodynamic control of the crystal growth, leading to spheroidal nanoparticles, seems to occur when additives which strongly interact with the nanoparticle surface are used. A thorough characterization of the materials was performed. Magnetic properties were investigated by Superconducting Quantum Interference Device and Vibrating Sample magnetometers. Based on the observed magnetic properties, the magnetite obtained using citrate appears to be a promising support for magnetically transportable catalysts.